Shotblast Type: | Shot Blasting |
---|---|
Shotblast Material: | Steel Shot |
Sandblasting Type: | Automatic Sandblasting |
Shotblast Application: | Guns and Tanks |
Sandblasting Method: | Dry Spray |
Sandblasting Applications: | Metallurgy |
Customization: |
---|
Suppliers with verified business licenses
Application: | Abrasive Refractory Industry |
---|---|
Function: | Descaling |
Particle Size: | Customer Requirement |
Hardness: | Superabrasive |
Density: | 7g/cm3 |
Microstructure: | Homogeneous Tempered Martensite or Troostite |
First. Introduction of S330 Steel Shot
S330 steel shot refers to a steel shot with a product diameter of 1.0mm. s330 can achieve good coverage in a short time. For various castings with high requirements on the surface of the workpiece, s330 steel shot has uniform hardness and good cleaning effect. ,Durable wear. The brightness of the cleaned workpiece is large, and the processing effect is very obvious.
Second, the advantages of S330 steel shot
1. Tight organization, uniform particle size, moderate hardness, strong toughness and impact resistance.
2. Good abrasion resistance, long life, and continuous and repeatable use.
3. Uniform product, good resilience, strong adhesion and fast cleaning speed.
4. The brightness of the cleaned workpiece is large, and the processing effect is very obvious.
Three, S330 steel shot composition table
mesh | mm | Specifications of steel shot | ||||||||||
SS-2.5 | SS-2.0 | SS-1.7 | SS-1.4 | SS-1.2 | SS-1.0 | SS-0.8 | SS-0.6 | SS-0.5 | SS-0.3 | SS-0.2 | ||
7 | 2.80 | All pass | ||||||||||
8 | 2.36 | All pass | ||||||||||
10 | 2.00 | 85%min | All pass | All pass | ||||||||
12 | 1.70 | 97%min | 85%min | 5%max | All pass | |||||||
14 | 1.40 | 97%min | 85%min | 5%max | All pass | |||||||
16 | 1.18 | 97%min | 85%min | 5%max | All pass | |||||||
18 | 1.00 | 96%min | 85%min | 5%max | All pass | |||||||
20 | 0.850 | 96%min | 85%min | 10%max | All pass | |||||||
25 | 0.710 | 96%min | 85%min | 10%max | ||||||||
30 | 0.600 | 96%min | 85%min | All pass | ||||||||
35 | 0.500 | 97%min | 10%max | |||||||||
40 | 0.425 | 85%min | All pass | |||||||||
45 | 0.355 | 97%min | 10%max | |||||||||
50 | 0.300 | 80%min | ||||||||||
80 | 0.180 | 90%min | 80%min | |||||||||
120 | 0.125 | 90%min | ||||||||||
200 | 0.075 | |||||||||||
325 | 0.045 | |||||||||||
SAE J444 | S-780 | S-660 | S-550 | S-460 | S-390 | S-330 | S-280 | S-230 | S-170 | S-110 | S-70 |
Name | Cast steel shot | Cast steel grit | Steel cut wire shot | Conditional cut wire shot | HQ cast steel shot | |
Chemical composition | C | 0.80-1.20% | 0.45-0.85% | 0.45-0.85% | 0.80-1.20% | |
Mn | 0.35-1.20% | 0.30-1.30% | 0.30-1.30% | 0.35-1.20% | ||
Si | ≥0.40 | 0.15-0.35% | 0.15-0.35% | ≥0.40 | ||
S | ≤0.05% | ≤0.05% | ≤0.05% | ≤0.05% | ||
P | ≤0.05% | ≤0.04% | ≤0.04% | ≤0.05% | ||
hardness | Routine:40-50HRC | GP steel grit 42-52HRC |
1.0mm:42-53HRC | 45-60HRC | Routine:42-47HRC Special:52-56HRC Special:56-60HRC |
|
Special:52-56HRC | GP steel grit 53-60HRC |
1.5mm:41-45HRC | ||||
Special:56-60HRC | GP steel grit 60-64HRC |
|||||
Hardness deviation | The max deviation range:±3.0HRC | |||||
Tensile intensity | - | 1300-2200Mpa | 2200-2800Mpa | - | ||
Durability | 2000-28000 times | 3300-4000times | 4000times | 2800-3300times | ||
Microstructure | Tempered martensite or sorbite | Deformed pearlite | Deformed sorbite | Tempered martensite or sorbite | ||
Density | 7.4g/cm3 | 7.6g/cm3 | 7.8g/cm3 | 7.8g/cm3 | 7.4g/cm3 | |
Bulk density | 4.4g/cm3 | 4.2g/cm3 | 4.5g/cm3 | 4.5g/cm3 | 4.4g/cm3 |