High Quality Low Carbon Steel Shot Used on Wire Rod Product

• Application: Abrasive Refractory Industry
• Function: Descaling
• Particle Size: Customer Requirement
• Hardness: Superabrasive
• Density: 7g/cm3
• Microstructure: Homogeneous Tempered Martensite or Troostite
• Model NO.: S330
• External Form: Round Shape
• Payment: T/T
• Samples: 500gram
• Transport Package: 25kg*40bags
• Specification: S70/110/170/230/280/330/390/460/550/660/780
• Trademark: Pumingwei
• Origin: China
• HS Code: 72051000
• Production Capacity: 60000t

Product Description

 

 

Product Description

Low Carbon Steel Shot
Low Hardness Extreme Durability Round Shape Safe on Delicate and Sensitive Parts Works in Standard Blast Equipment Little to No Dusting Won't Damage Part Details No Work Hardening of the Part Resists Breaking Down No Metal Removal from Part Surface Applications Deburring Delicate Machined Parts and Stampings Cleaning Investment Castings Remove Release Agent Build-up on Molds Corrosion Removal Remove Heat Treat Scale Deflashing Die Cast Aluminum Parts
Hight Carbon Steel Shot
Is used in wheel blasting equipment. It also gives a hammered or peened effect for use on ferrous castings and fabrication  Our High-carbon steel shot is a very powerful abrasive for the surface treatment of metallic products. In contrast to low carbon steel shot round, this product has a higher beam intensity and thus enables faster working.  Steel shot also has a use in the removal of scale, rust and surface contaminant and used foundries for de-burring or de-flashing of castings and cleaning moulds.

Product Parameters

mesh

mm

Specifications of steel shot

SS-2.5

SS-2.0

SS-1.7

SS-1.4

SS-1.2

SS-1.0

SS-0.8

SS-0.6

SS-0.5

SS-0.3

SS-0.2

7

2.80

All pass

8

2.36

All pass

10

2.00

85%min

All pass

All pass

12

1.70

97%min

85%min

5%max

All pass

14

1.40

97%min

85%min

5%max

All pass

16

1.18

97%min

85%min

5%max

All pass

18

1.00

96%min

85%min

5%max

All pass

20

0.850

96%min

85%min

10%max

All pass

25

0.710

96%min

85%min

10%max

30

0.600

96%min

85%min

All pass

35

0.500

97%min

10%max

40

0.425

85%min

All pass

45

0.355

97%min

10%max

50

0.300

80%min

80

0.180

90%min

80%min

120

0.125

90%min

200

0.075

325

0.045

SAE J444

S-780

S-660

S-550

S-460

S-390

S-330

S-280

S-230

S-170

S-110

S-70

Name		Cast steel shot	Cast steel grit	Steel cut wire shot	Conditional cut wire shot	HQ cast steel shot
Chemical composition	C	0.80-1.20%		0.45-0.85%	0.45-0.85%	0.80-1.20%
	Mn	0.35-1.20%		0.30-1.30%	0.30-1.30%	0.35-1.20%
	Si	≥0.40		0.15-0.35%	0.15-0.35%	≥0.40
	S	≤0.05%		≤0.05%	≤0.05%	≤0.05%
	P	≤0.05%		≤0.04%	≤0.04%	≤0.05%
hardness		Routine:40-50HRC	GP steel grit 42-52HRC	1.0mm:42-53HRC	45-60HRC	Routine:42-47HRC Special:52-56HRC Special:56-60HRC
		Special:52-56HRC	GP steel grit 53-60HRC	1.5mm:41-45HRC
		Special:56-60HRC	GP steel grit 60-64HRC
Hardness deviation		The max deviation range:±3.0HRC
Tensile intensity		-		1300-2200Mpa	2200-2800Mpa	-
Durability		2000-28000 times		3300-4000times	4000times	2800-3300times
Microstructure		Tempered martensite or sorbite		Deformed pearlite	Deformed sorbite	Tempered martensite or sorbite
Density		7.4g/cm^3	7.6g/cm^3	7.8g/cm^3	7.8g/cm^3	7.4g/cm^3
Bulk density		4.4g/cm^3	4.2g/cm^3	4.5g/cm^3	4.5g/cm^3	4.4g/cm^3